MakeItFrom.com
Menu (ESC)

EN 2.4964 Cobalt vs. 6005 Aluminum

EN 2.4964 cobalt belongs to the cobalt alloys classification, while 6005 aluminum belongs to the aluminum alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 2.4964 cobalt and the bottom bar is 6005 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
68
Elongation at Break, % 40
9.5 to 17
Fatigue Strength, MPa 220
55 to 95
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 86
26
Tensile Strength: Ultimate (UTS), MPa 960
190 to 310
Tensile Strength: Yield (Proof), MPa 390
100 to 280

Thermal Properties

Latent Heat of Fusion, J/g 290
410
Melting Completion (Liquidus), °C 1630
650
Melting Onset (Solidus), °C 1550
610
Specific Heat Capacity, J/kg-K 400
900
Thermal Conductivity, W/m-K 15
180 to 200
Thermal Expansion, µm/m-K 12
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
54
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
180

Otherwise Unclassified Properties

Density, g/cm3 9.6
2.7
Embodied Carbon, kg CO2/kg material 9.8
8.3
Embodied Energy, MJ/kg 140
150
Embodied Water, L/kg 450
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 310
27 to 36
Resilience: Unit (Modulus of Resilience), kJ/m3 340
77 to 550
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 21
51
Strength to Weight: Axial, points 28
20 to 32
Strength to Weight: Bending, points 23
28 to 38
Thermal Diffusivity, mm2/s 3.9
74 to 83
Thermal Shock Resistance, points 25
8.6 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
97.5 to 99
Carbon (C), % 0.050 to 0.15
0
Chromium (Cr), % 19 to 21
0 to 0.1
Cobalt (Co), % 46.4 to 58
0
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 0 to 3.0
0 to 0.35
Magnesium (Mg), % 0
0.4 to 0.6
Manganese (Mn), % 0 to 2.0
0 to 0.1
Nickel (Ni), % 9.0 to 11
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.4
0.6 to 0.9
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
0 to 0.1
Tungsten (W), % 14 to 16
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15