EN 2.4964 Cobalt vs. EN 1.7701 Steel

EN 2.4964 cobalt belongs to the cobalt alloys classification, while EN 1.7701 steel belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 2.4964 cobalt and the bottom bar is EN 1.7701 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
73
Tensile Strength: Ultimate (UTS), MPa 960
670 to 2010

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Melting Completion (Liquidus), °C 1630
1460
Melting Onset (Solidus), °C 1550
1420
Specific Heat Capacity, J/kg-K 400
470
Thermal Conductivity, W/m-K 15
44
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
8.5

Otherwise Unclassified Properties

Density, g/cm3 9.6
7.8
Embodied Carbon, kg CO2/kg material 9.8
1.9
Embodied Energy, MJ/kg 140
26
Embodied Water, L/kg 450
52

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 28
24 to 71
Strength to Weight: Bending, points 23
22 to 45
Thermal Diffusivity, mm2/s 3.9
12
Thermal Shock Resistance, points 25
20 to 59

Alloy Composition

Carbon (C), % 0.050 to 0.15
0.48 to 0.56
Chromium (Cr), % 19 to 21
0.9 to 1.2
Cobalt (Co), % 46.4 to 58
0
Iron (Fe), % 0 to 3.0
96.2 to 97.7
Manganese (Mn), % 0 to 2.0
0.7 to 1.1
Molybdenum (Mo), % 0
0.15 to 0.3
Nickel (Ni), % 9.0 to 11
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.025
Tungsten (W), % 14 to 16
0
Vanadium (V), % 0
0.1 to 0.2