EN AC-21100 Aluminum vs. 520.0 Aluminum
Both EN AC-21100 aluminum and 520.0 aluminum are aluminum alloys. They have 90% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN AC-21100 aluminum and the bottom bar is 520.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 100 to 110 | |
| 75 |
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 66 |
| Elongation at Break, % | 6.2 to 7.3 | |
| 14 |
| Fatigue Strength, MPa | 79 to 87 | |
| 55 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 25 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 350 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 210 to 240 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 170 |
| Melting Completion (Liquidus), °C | 670 | |
| 600 |
| Melting Onset (Solidus), °C | 550 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 910 |
| Thermal Conductivity, W/m-K | 130 | |
| 87 |
| Thermal Expansion, µm/m-K | 23 | |
| 25 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 34 | |
| 21 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 72 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 9.5 |
| Density, g/cm3 | 3.0 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 9.8 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1150 | |
| 1170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 to 21 | |
| 39 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 to 400 | |
| 230 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 46 | |
| 52 |
| Strength to Weight: Axial, points | 31 to 33 | |
| 35 |
| Strength to Weight: Bending, points | 36 to 37 | |
| 41 |
| Thermal Diffusivity, mm2/s | 48 | |
| 37 |
| Thermal Shock Resistance, points | 15 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 93.4 to 95.7 | |
| 87.9 to 90.5 |
| Copper (Cu), % | 4.2 to 5.2 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.19 | |
| 0 to 0.3 |
| Magnesium (Mg), % | 0 | |
| 9.5 to 10.6 |
| Manganese (Mn), % | 0 to 0.55 | |
| 0 to 0.15 |
| Silicon (Si), % | 0 to 0.18 | |
| 0 to 0.25 |
| Titanium (Ti), % | 0.15 to 0.3 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 0.070 | |
| 0 to 0.15 |
| Residuals, % | 0 to 0.1 | |
| 0 to 0.15 |