EN AC-21100 Aluminum vs. SAE-AISI T1 Steel

EN AC-21100 aluminum belongs to the aluminum alloys classification, while SAE-AISI T1 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN AC-21100 aluminum and the bottom bar is SAE-AISI T1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
200
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 27
80
Tensile Strength: Ultimate (UTS), MPa 340 to 350
770 to 2130

Thermal Properties

Latent Heat of Fusion, J/g 390
240
Melting Completion (Liquidus), °C 670
1810
Melting Onset (Solidus), °C 550
1750
Specific Heat Capacity, J/kg-K 880
410
Thermal Conductivity, W/m-K 130
20
Thermal Expansion, µm/m-K 23
12

Otherwise Unclassified Properties

Base Metal Price, % relative 11
45
Density, g/cm3 3.0
9.3
Embodied Carbon, kg CO2/kg material 8.0
8.2
Embodied Energy, MJ/kg 150
130
Embodied Water, L/kg 1150
90

Common Calculations

Stiffness to Weight: Axial, points 13
12
Stiffness to Weight: Bending, points 46
21
Strength to Weight: Axial, points 31 to 33
23 to 64
Strength to Weight: Bending, points 36 to 37
20 to 40
Thermal Diffusivity, mm2/s 48
5.2
Thermal Shock Resistance, points 15
23 to 64

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 93.4 to 95.7
0
Carbon (C), % 0
0.65 to 0.8
Chromium (Cr), % 0
3.8 to 4.5
Copper (Cu), % 4.2 to 5.2
0 to 0.25
Iron (Fe), % 0 to 0.19
73.2 to 77.2
Manganese (Mn), % 0 to 0.55
0.1 to 0.4
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.18
0.2 to 0.4
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0.15 to 0.3
0
Tungsten (W), % 0
17.3 to 18.8
Vanadium (V), % 0
0.9 to 1.3
Zinc (Zn), % 0 to 0.070
0
Residuals, % 0 to 0.1
0