EN AC-21100 Aluminum vs. S44330 Stainless Steel

EN AC-21100 aluminum belongs to the aluminum alloys classification, while S44330 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN AC-21100 aluminum and the bottom bar is S44330 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 100 to 110
160
Elastic (Young's, Tensile) Modulus, GPa 71
200
Elongation at Break, % 6.2 to 7.3
25
Fatigue Strength, MPa 79 to 87
160
Poisson's Ratio 0.33
0.27
Shear Modulus, GPa 27
78
Tensile Strength: Ultimate (UTS), MPa 340 to 350
440
Tensile Strength: Yield (Proof), MPa 210 to 240
230

Thermal Properties

Latent Heat of Fusion, J/g 390
290
Maximum Temperature: Mechanical, °C 170
990
Melting Completion (Liquidus), °C 670
1440
Melting Onset (Solidus), °C 550
1390
Specific Heat Capacity, J/kg-K 880
480
Thermal Conductivity, W/m-K 130
21
Thermal Expansion, µm/m-K 23
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 34
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 100
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 11
13
Density, g/cm3 3.0
7.7
Embodied Carbon, kg CO2/kg material 8.0
2.8
Embodied Energy, MJ/kg 150
40
Embodied Water, L/kg 1150
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19 to 21
91
Resilience: Unit (Modulus of Resilience), kJ/m3 300 to 400
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 46
25
Strength to Weight: Axial, points 31 to 33
16
Strength to Weight: Bending, points 36 to 37
17
Thermal Diffusivity, mm2/s 48
5.7
Thermal Shock Resistance, points 15
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 93.4 to 95.7
0
Carbon (C), % 0
0 to 0.025
Chromium (Cr), % 0
20 to 23
Copper (Cu), % 4.2 to 5.2
0.3 to 0.8
Iron (Fe), % 0 to 0.19
72.5 to 79.7
Manganese (Mn), % 0 to 0.55
0 to 1.0
Niobium (Nb), % 0
0 to 0.8
Nitrogen (N), % 0
0 to 0.025
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.18
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0.15 to 0.3
0 to 0.8
Zinc (Zn), % 0 to 0.070
0
Residuals, % 0 to 0.1
0