EN AC-43200 Aluminum vs. EN AC-51300 Aluminum

Both EN AC-43200 aluminum and EN AC-51300 aluminum are aluminum alloys. They have 90% of their average alloy composition in common.

For each property being compared, the top bar is EN AC-43200 aluminum and the bottom bar is EN AC-51300 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 60 to 88
65
Elastic (Young's, Tensile) Modulus, GPa 72
67
Elongation at Break, % 1.1
3.7
Fatigue Strength, MPa 67
78
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 27
25
Tensile Strength: Ultimate (UTS), MPa 190 to 260
190
Tensile Strength: Yield (Proof), MPa 97 to 220
110

Thermal Properties

Latent Heat of Fusion, J/g 540
400
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 600
640
Melting Onset (Solidus), °C 590
600
Specific Heat Capacity, J/kg-K 900
910
Thermal Conductivity, W/m-K 140
110
Thermal Expansion, µm/m-K 22
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 34
31
Electrical Conductivity: Equal Weight (Specific), % IACS 120
100

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.6
2.7
Embodied Carbon, kg CO2/kg material 7.8
9.1
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1070
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 1.8 to 2.7
6.1
Resilience: Unit (Modulus of Resilience), kJ/m3 66 to 330
87
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 54
51
Strength to Weight: Axial, points 20 to 28
20
Strength to Weight: Bending, points 28 to 35
28
Thermal Diffusivity, mm2/s 59
45
Thermal Shock Resistance, points 8.8 to 12
8.6

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 86.1 to 90.8
91.4 to 95.5
Copper (Cu), % 0 to 0.35
0 to 0.1
Iron (Fe), % 0 to 0.65
0 to 0.55
Lead (Pb), % 0 to 0.1
0
Magnesium (Mg), % 0.2 to 0.45
4.5 to 6.5
Manganese (Mn), % 0 to 0.55
0 to 0.45
Nickel (Ni), % 0 to 0.15
0
Silicon (Si), % 9.0 to 11
0 to 0.55
Titanium (Ti), % 0 to 0.2
0 to 0.2
Zinc (Zn), % 0 to 0.35
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.15