EN AC-43500 Aluminum vs. 1080 Aluminum
Both EN AC-43500 aluminum and 1080 aluminum are aluminum alloys. They have 89% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN AC-43500 aluminum and the bottom bar is 1080 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 68 |
| Elongation at Break, % | 4.5 to 13 | |
| 4.6 to 40 |
| Fatigue Strength, MPa | 62 to 100 | |
| 21 to 48 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 300 | |
| 72 to 130 |
| Tensile Strength: Yield (Proof), MPa | 140 to 170 | |
| 17 to 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 550 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 170 |
| Melting Completion (Liquidus), °C | 600 | |
| 640 |
| Melting Onset (Solidus), °C | 590 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 140 | |
| 230 |
| Thermal Expansion, µm/m-K | 22 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 38 | |
| 61 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 200 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.6 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 7.8 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1070 | |
| 1200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 26 | |
| 4.7 to 21 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 200 | |
| 2.1 to 100 |
| Stiffness to Weight: Axial, points | 16 | |
| 14 |
| Stiffness to Weight: Bending, points | 54 | |
| 50 |
| Strength to Weight: Axial, points | 24 to 33 | |
| 7.4 to 14 |
| Strength to Weight: Bending, points | 32 to 39 | |
| 14 to 22 |
| Thermal Diffusivity, mm2/s | 60 | |
| 94 |
| Thermal Shock Resistance, points | 10 to 14 | |
| 3.2 to 6.0 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 86.4 to 90.5 | |
| 99.8 to 100 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.030 |
| Gallium (Ga), % | 0 | |
| 0 to 0.030 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 0.1 to 0.6 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0.4 to 0.8 | |
| 0 to 0.020 |
| Silicon (Si), % | 9.0 to 11.5 | |
| 0 to 0.15 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 0 to 0.070 | |
| 0 to 0.030 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.020 |