EN AC-44000 Aluminum vs. ACI-ASTM CA15 Steel

EN AC-44000 aluminum belongs to the aluminum alloys classification, while ACI-ASTM CA15 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN AC-44000 aluminum and the bottom bar is ACI-ASTM CA15 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 51
220
Elastic (Young's, Tensile) Modulus, GPa 71
190
Elongation at Break, % 7.3
21
Fatigue Strength, MPa 64
370
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 27
76
Tensile Strength: Ultimate (UTS), MPa 180
700
Tensile Strength: Yield (Proof), MPa 86
570

Thermal Properties

Latent Heat of Fusion, J/g 560
280
Maximum Temperature: Mechanical, °C 170
750
Melting Completion (Liquidus), °C 590
1440
Melting Onset (Solidus), °C 590
1500
Specific Heat Capacity, J/kg-K 910
480
Thermal Conductivity, W/m-K 140
25
Thermal Expansion, µm/m-K 21
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 36
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 130
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
7.5
Density, g/cm3 2.5
7.7
Embodied Carbon, kg CO2/kg material 7.8
2.0
Embodied Energy, MJ/kg 150
28
Embodied Water, L/kg 1070
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
140
Resilience: Unit (Modulus of Resilience), kJ/m3 51
820
Stiffness to Weight: Axial, points 16
14
Stiffness to Weight: Bending, points 55
25
Strength to Weight: Axial, points 20
25
Strength to Weight: Bending, points 28
23
Thermal Diffusivity, mm2/s 61
6.7
Thermal Shock Resistance, points 8.4
26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.1 to 90
0
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
11.5 to 14
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.19
81.8 to 88.5
Magnesium (Mg), % 0 to 0.45
0
Manganese (Mn), % 0 to 0.1
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 1.0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 10 to 11.8
0 to 1.5
Sulfur (S), % 0
0 to 0.040
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.070
0
Residuals, % 0 to 0.1
0