EN AC-44000 Aluminum vs. EN 1.3961 Alloy

EN AC-44000 aluminum belongs to the aluminum alloys classification, while EN 1.3961 alloy belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN AC-44000 aluminum and the bottom bar is EN 1.3961 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
190
Elongation at Break, % 7.3
31
Poisson's Ratio 0.33
0.3
Shear Modulus, GPa 27
72
Tensile Strength: Ultimate (UTS), MPa 180
450
Tensile Strength: Yield (Proof), MPa 86
310

Thermal Properties

Latent Heat of Fusion, J/g 560
270
Melting Completion (Liquidus), °C 590
1430
Melting Onset (Solidus), °C 590
1390
Specific Heat Capacity, J/kg-K 910
460
Thermal Expansion, µm/m-K 21
1.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
25
Density, g/cm3 2.5
8.2
Embodied Carbon, kg CO2/kg material 7.8
4.8
Embodied Energy, MJ/kg 150
66
Embodied Water, L/kg 1070
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
130
Resilience: Unit (Modulus of Resilience), kJ/m3 51
250
Stiffness to Weight: Axial, points 16
13
Stiffness to Weight: Bending, points 55
23
Strength to Weight: Axial, points 20
15
Strength to Weight: Bending, points 28
16
Thermal Shock Resistance, points 8.4
130

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.1 to 90
0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
0 to 0.25
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.19
60.7 to 65
Magnesium (Mg), % 0 to 0.45
0
Manganese (Mn), % 0 to 0.1
0 to 0.5
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 0
35 to 37
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 10 to 11.8
0 to 0.5
Sulfur (S), % 0
0 to 0.020
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.070
0
Residuals, % 0 to 0.1
0