EN AC-44000 Aluminum vs. EN 1.4588 Stainless Steel

EN AC-44000 aluminum belongs to the aluminum alloys classification, while EN 1.4588 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN AC-44000 aluminum and the bottom bar is EN 1.4588 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 51
160
Elastic (Young's, Tensile) Modulus, GPa 71
200
Elongation at Break, % 7.3
34
Fatigue Strength, MPa 64
190
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 27
80
Tensile Strength: Ultimate (UTS), MPa 180
540
Tensile Strength: Yield (Proof), MPa 86
240

Thermal Properties

Latent Heat of Fusion, J/g 560
300
Maximum Temperature: Mechanical, °C 170
1100
Melting Completion (Liquidus), °C 590
1450
Melting Onset (Solidus), °C 590
1410
Specific Heat Capacity, J/kg-K 910
460
Thermal Conductivity, W/m-K 140
15
Thermal Expansion, µm/m-K 21
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 36
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 130
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
33
Density, g/cm3 2.5
8.1
Embodied Carbon, kg CO2/kg material 7.8
6.2
Embodied Energy, MJ/kg 150
84
Embodied Water, L/kg 1070
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
150
Resilience: Unit (Modulus of Resilience), kJ/m3 51
140
Stiffness to Weight: Axial, points 16
14
Stiffness to Weight: Bending, points 55
24
Strength to Weight: Axial, points 20
18
Strength to Weight: Bending, points 28
18
Thermal Diffusivity, mm2/s 61
4.0
Thermal Shock Resistance, points 8.4
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.1 to 90
0
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
19 to 21
Copper (Cu), % 0 to 0.050
0.5 to 1.5
Iron (Fe), % 0 to 0.19
41.2 to 50.4
Magnesium (Mg), % 0 to 0.45
0
Manganese (Mn), % 0 to 0.1
0 to 2.0
Molybdenum (Mo), % 0
6.0 to 7.0
Nickel (Ni), % 0
24 to 26
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 10 to 11.8
0 to 1.0
Sulfur (S), % 0
0 to 0.020
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.070
0
Residuals, % 0 to 0.1
0