EN AC-44000 Aluminum vs. CC484K Bronze

EN AC-44000 aluminum belongs to the aluminum alloys classification, while CC484K bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN AC-44000 aluminum and the bottom bar is CC484K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 51
100
Elastic (Young's, Tensile) Modulus, GPa 71
110
Elongation at Break, % 7.3
11
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 27
41
Tensile Strength: Ultimate (UTS), MPa 180
330
Tensile Strength: Yield (Proof), MPa 86
200

Thermal Properties

Latent Heat of Fusion, J/g 560
190
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 590
1000
Melting Onset (Solidus), °C 590
870
Specific Heat Capacity, J/kg-K 910
370
Thermal Conductivity, W/m-K 140
70
Thermal Expansion, µm/m-K 21
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 36
9.1
Electrical Conductivity: Equal Weight (Specific), % IACS 130
9.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
37
Density, g/cm3 2.5
8.7
Embodied Carbon, kg CO2/kg material 7.8
3.9
Embodied Energy, MJ/kg 150
64
Embodied Water, L/kg 1070
400

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
32
Resilience: Unit (Modulus of Resilience), kJ/m3 51
180
Stiffness to Weight: Axial, points 16
6.9
Stiffness to Weight: Bending, points 55
18
Strength to Weight: Axial, points 20
10
Strength to Weight: Bending, points 28
12
Thermal Diffusivity, mm2/s 61
22
Thermal Shock Resistance, points 8.4
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.1 to 90
0 to 0.010
Antimony (Sb), % 0
0 to 0.1
Copper (Cu), % 0 to 0.050
84.5 to 87.5
Iron (Fe), % 0 to 0.19
0 to 0.2
Lead (Pb), % 0
0 to 0.3
Magnesium (Mg), % 0 to 0.45
0
Manganese (Mn), % 0 to 0.1
0 to 0.2
Nickel (Ni), % 0
1.5 to 2.5
Phosphorus (P), % 0
0.050 to 0.4
Silicon (Si), % 10 to 11.8
0 to 0.010
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
11 to 13
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.070
0 to 0.4
Residuals, % 0 to 0.1
0