EN AC-44000 Aluminum vs. C17300 Copper

EN AC-44000 aluminum belongs to the aluminum alloys classification, while C17300 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN AC-44000 aluminum and the bottom bar is C17300 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
120
Elongation at Break, % 7.3
3.0 to 23
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 27
45
Tensile Strength: Ultimate (UTS), MPa 180
500 to 1380
Tensile Strength: Yield (Proof), MPa 86
160 to 1200

Thermal Properties

Latent Heat of Fusion, J/g 560
230
Maximum Temperature: Mechanical, °C 170
270
Melting Completion (Liquidus), °C 590
980
Melting Onset (Solidus), °C 590
870
Specific Heat Capacity, J/kg-K 910
380
Thermal Conductivity, W/m-K 140
110
Thermal Expansion, µm/m-K 21
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 36
22
Electrical Conductivity: Equal Weight (Specific), % IACS 130
23

Otherwise Unclassified Properties

Density, g/cm3 2.5
8.8
Embodied Carbon, kg CO2/kg material 7.8
9.4
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1070
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
40 to 88
Resilience: Unit (Modulus of Resilience), kJ/m3 51
110 to 5410
Stiffness to Weight: Axial, points 16
7.6
Stiffness to Weight: Bending, points 55
19
Strength to Weight: Axial, points 20
16 to 44
Strength to Weight: Bending, points 28
16 to 31
Thermal Diffusivity, mm2/s 61
32
Thermal Shock Resistance, points 8.4
17 to 48

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.1 to 90
0 to 0.2
Beryllium (Be), % 0
1.8 to 2.0
Copper (Cu), % 0 to 0.050
95.5 to 97.8
Iron (Fe), % 0 to 0.19
0 to 0.4
Lead (Pb), % 0
0.2 to 0.6
Magnesium (Mg), % 0 to 0.45
0
Manganese (Mn), % 0 to 0.1
0
Nickel (Ni), % 0
0.2 to 0.6
Silicon (Si), % 10 to 11.8
0 to 0.2
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.070
0
Residuals, % 0 to 0.1
0 to 0.5