EN AC-44000 Aluminum vs. C35000 Brass

EN AC-44000 aluminum belongs to the aluminum alloys classification, while C35000 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN AC-44000 aluminum and the bottom bar is C35000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
100
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 27
40
Tensile Strength: Ultimate (UTS), MPa 180
340 to 650

Thermal Properties

Latent Heat of Fusion, J/g 560
170
Maximum Temperature: Mechanical, °C 170
120
Melting Completion (Liquidus), °C 590
920
Melting Onset (Solidus), °C 590
890
Specific Heat Capacity, J/kg-K 910
380
Thermal Conductivity, W/m-K 140
120
Thermal Expansion, µm/m-K 21
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 36
26
Electrical Conductivity: Equal Weight (Specific), % IACS 130
29

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
23
Density, g/cm3 2.5
8.1
Embodied Carbon, kg CO2/kg material 7.8
2.7
Embodied Energy, MJ/kg 150
45
Embodied Water, L/kg 1070
320

Common Calculations

Stiffness to Weight: Axial, points 16
7.1
Stiffness to Weight: Bending, points 55
19
Strength to Weight: Axial, points 20
12 to 22
Strength to Weight: Bending, points 28
13 to 21
Thermal Diffusivity, mm2/s 61
37
Thermal Shock Resistance, points 8.4
11 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.1 to 90
0
Copper (Cu), % 0 to 0.050
60 to 63
Iron (Fe), % 0 to 0.19
0 to 0.1
Lead (Pb), % 0
0.8 to 2.0
Magnesium (Mg), % 0 to 0.45
0
Manganese (Mn), % 0 to 0.1
0
Silicon (Si), % 10 to 11.8
0
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.070
34.5 to 39.2
Residuals, % 0 to 0.1
0 to 0.4