EN AC-44000 Aluminum vs. R30075 Cobalt

EN AC-44000 aluminum belongs to the aluminum alloys classification, while R30075 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN AC-44000 aluminum and the bottom bar is R30075 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
210 to 250
Elongation at Break, % 7.3
12
Fatigue Strength, MPa 64
250 to 840
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 27
82 to 98
Tensile Strength: Ultimate (UTS), MPa 180
780 to 1280
Tensile Strength: Yield (Proof), MPa 86
480 to 840

Thermal Properties

Latent Heat of Fusion, J/g 560
320
Melting Completion (Liquidus), °C 590
1360
Melting Onset (Solidus), °C 590
1290
Specific Heat Capacity, J/kg-K 910
450
Thermal Conductivity, W/m-K 140
13
Thermal Expansion, µm/m-K 21
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 36
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 130
2.1

Otherwise Unclassified Properties

Density, g/cm3 2.5
8.4
Embodied Carbon, kg CO2/kg material 7.8
8.1
Embodied Energy, MJ/kg 150
110
Embodied Water, L/kg 1070
530

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
84 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 51
560 to 1410
Stiffness to Weight: Axial, points 16
14 to 17
Stiffness to Weight: Bending, points 55
24 to 25
Strength to Weight: Axial, points 20
26 to 42
Strength to Weight: Bending, points 28
22 to 31
Thermal Diffusivity, mm2/s 61
3.5
Thermal Shock Resistance, points 8.4
21 to 29

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.1 to 90
0 to 0.1
Boron (B), % 0
0 to 0.010
Carbon (C), % 0
0 to 0.35
Chromium (Cr), % 0
27 to 30
Cobalt (Co), % 0
58.7 to 68
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.19
0 to 0.75
Magnesium (Mg), % 0 to 0.45
0
Manganese (Mn), % 0 to 0.1
0 to 1.0
Molybdenum (Mo), % 0
5.0 to 7.0
Nickel (Ni), % 0
0 to 0.5
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 10 to 11.8
0 to 1.0
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0 to 0.15
0 to 0.1
Tungsten (W), % 0
0 to 0.2
Zinc (Zn), % 0 to 0.070
0
Residuals, % 0 to 0.1
0