EN AC-45000 Aluminum vs. 852.0 Aluminum

Both EN AC-45000 aluminum and 852.0 aluminum are aluminum alloys. They have a moderately high 90% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN AC-45000 aluminum and the bottom bar is 852.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 77
64
Elastic (Young's, Tensile) Modulus, GPa 73
70
Elongation at Break, % 1.1
3.4
Fatigue Strength, MPa 75
73
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 27
26
Tensile Strength: Ultimate (UTS), MPa 180
200
Tensile Strength: Yield (Proof), MPa 110
150

Thermal Properties

Latent Heat of Fusion, J/g 470
370
Maximum Temperature: Mechanical, °C 180
190
Melting Completion (Liquidus), °C 640
640
Melting Onset (Solidus), °C 520
210
Specific Heat Capacity, J/kg-K 870
840
Thermal Conductivity, W/m-K 120
180
Thermal Expansion, µm/m-K 22
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
45
Electrical Conductivity: Equal Weight (Specific), % IACS 81
130

Otherwise Unclassified Properties

Base Metal Price, % relative 11
15
Density, g/cm3 3.0
3.2
Embodied Carbon, kg CO2/kg material 7.7
8.5
Embodied Energy, MJ/kg 140
160
Embodied Water, L/kg 1070
1150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 1.7
6.2
Resilience: Unit (Modulus of Resilience), kJ/m3 80
160
Stiffness to Weight: Axial, points 14
12
Stiffness to Weight: Bending, points 47
43
Strength to Weight: Axial, points 17
17
Strength to Weight: Bending, points 24
24
Thermal Diffusivity, mm2/s 47
65
Thermal Shock Resistance, points 8.0
8.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 82.2 to 91.8
86.6 to 91.3
Chromium (Cr), % 0 to 0.15
0
Copper (Cu), % 3.0 to 5.0
1.7 to 2.3
Iron (Fe), % 0 to 1.0
0 to 0.7
Lead (Pb), % 0 to 0.3
0
Magnesium (Mg), % 0 to 0.55
0.6 to 0.9
Manganese (Mn), % 0.2 to 0.65
0 to 0.1
Nickel (Ni), % 0 to 0.45
0.9 to 1.5
Silicon (Si), % 5.0 to 7.0
0 to 0.4
Tin (Sn), % 0 to 0.15
5.5 to 7.0
Titanium (Ti), % 0 to 0.25
0 to 0.2
Zinc (Zn), % 0 to 2.0
0
Residuals, % 0 to 0.35
0 to 0.3