EN AC-45300 Aluminum vs. ZA-12
EN AC-45300 aluminum belongs to the aluminum alloys classification, while ZA-12 belongs to the zinc alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN AC-45300 aluminum and the bottom bar is ZA-12.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 94 to 120 | |
| 89 to 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 83 |
| Elongation at Break, % | 1.0 to 2.8 | |
| 1.6 to 5.3 |
| Fatigue Strength, MPa | 59 to 72 | |
| 73 to 120 |
| Poisson's Ratio | 0.33 | |
| 0.26 |
| Shear Modulus, GPa | 27 | |
| 33 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 290 | |
| 260 to 400 |
| Tensile Strength: Yield (Proof), MPa | 150 to 230 | |
| 210 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 470 | |
| 120 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 100 |
| Melting Completion (Liquidus), °C | 630 | |
| 430 |
| Melting Onset (Solidus), °C | 590 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 450 |
| Thermal Conductivity, W/m-K | 150 | |
| 120 |
| Thermal Expansion, µm/m-K | 22 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 36 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 42 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 11 |
| Density, g/cm3 | 2.7 | |
| 6.0 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 3.4 |
| Embodied Energy, MJ/kg | 150 | |
| 64 |
| Embodied Water, L/kg | 1120 | |
| 440 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.7 to 5.6 | |
| 4.0 to 20 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 390 | |
| 260 to 620 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 50 | |
| 24 |
| Strength to Weight: Axial, points | 23 to 29 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 30 to 35 | |
| 15 to 20 |
| Thermal Diffusivity, mm2/s | 60 | |
| 43 |
| Thermal Shock Resistance, points | 10 to 13 | |
| 9.4 to 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 90.2 to 94.2 | |
| 10.5 to 11.5 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Copper (Cu), % | 1.0 to 1.5 | |
| 0.5 to 1.2 |
| Iron (Fe), % | 0 to 0.65 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 to 0.15 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0.35 to 0.65 | |
| 0.015 to 0.030 |
| Manganese (Mn), % | 0 to 0.55 | |
| 0 |
| Nickel (Ni), % | 0 to 0.25 | |
| 0 to 0.020 |
| Silicon (Si), % | 4.5 to 5.5 | |
| 0 to 0.060 |
| Tin (Sn), % | 0 to 0.050 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 0.15 | |
| 87.1 to 89 |
| Residuals, % | 0 to 0.15 | |
| 0 |