EN AC-46400 Aluminum vs. 224.0 Aluminum
Both EN AC-46400 aluminum and 224.0 aluminum are aluminum alloys. They have 90% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is EN AC-46400 aluminum and the bottom bar is 224.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 71 |
| Elongation at Break, % | 1.1 to 1.7 | |
| 4.0 to 10 |
| Fatigue Strength, MPa | 75 to 85 | |
| 86 to 120 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 170 to 310 | |
| 380 to 420 |
| Tensile Strength: Yield (Proof), MPa | 110 to 270 | |
| 280 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 520 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 220 |
| Melting Completion (Liquidus), °C | 610 | |
| 650 |
| Melting Onset (Solidus), °C | 570 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 870 |
| Thermal Conductivity, W/m-K | 130 | |
| 120 |
| Thermal Expansion, µm/m-K | 22 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 33 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 95 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 11 |
| Density, g/cm3 | 2.7 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 7.8 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1070 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 1.7 to 4.9 | |
| 16 to 35 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 82 to 500 | |
| 540 to 770 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 52 | |
| 45 |
| Strength to Weight: Axial, points | 18 to 32 | |
| 35 to 38 |
| Strength to Weight: Bending, points | 26 to 38 | |
| 38 to 41 |
| Thermal Diffusivity, mm2/s | 55 | |
| 47 |
| Thermal Shock Resistance, points | 7.8 to 14 | |
| 17 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 85.4 to 90.5 | |
| 93 to 95.2 |
| Copper (Cu), % | 0.8 to 1.3 | |
| 4.5 to 5.5 |
| Iron (Fe), % | 0 to 0.8 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Magnesium (Mg), % | 0.25 to 0.65 | |
| 0 |
| Manganese (Mn), % | 0.15 to 0.55 | |
| 0.2 to 0.5 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Silicon (Si), % | 8.3 to 9.7 | |
| 0 to 0.060 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.35 |
| Vanadium (V), % | 0 | |
| 0.050 to 0.15 |
| Zinc (Zn), % | 0 to 0.8 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0.1 to 0.25 |
| Residuals, % | 0 to 0.25 | |
| 0 to 0.1 |