EN AC-46400 Aluminum vs. Grade Ti-Pd8A Titanium
EN AC-46400 aluminum belongs to the aluminum alloys classification, while grade Ti-Pd8A titanium belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN AC-46400 aluminum and the bottom bar is grade Ti-Pd8A titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 77 to 120 | |
| 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 110 |
| Elongation at Break, % | 1.1 to 1.7 | |
| 13 |
| Fatigue Strength, MPa | 75 to 85 | |
| 260 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 27 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 170 to 310 | |
| 500 |
| Tensile Strength: Yield (Proof), MPa | 110 to 270 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 520 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 320 |
| Melting Completion (Liquidus), °C | 610 | |
| 1660 |
| Melting Onset (Solidus), °C | 570 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 540 |
| Thermal Conductivity, W/m-K | 130 | |
| 21 |
| Thermal Expansion, µm/m-K | 22 | |
| 8.7 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 33 | |
| 3.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 6.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 7.8 | |
| 49 |
| Embodied Energy, MJ/kg | 150 | |
| 840 |
| Embodied Water, L/kg | 1070 | |
| 520 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 1.7 to 4.9 | |
| 65 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 82 to 500 | |
| 880 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 52 | |
| 35 |
| Strength to Weight: Axial, points | 18 to 32 | |
| 31 |
| Strength to Weight: Bending, points | 26 to 38 | |
| 31 |
| Thermal Diffusivity, mm2/s | 55 | |
| 8.6 |
| Thermal Shock Resistance, points | 7.8 to 14 | |
| 39 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 85.4 to 90.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0.8 to 1.3 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.8 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Magnesium (Mg), % | 0.25 to 0.65 | |
| 0 |
| Manganese (Mn), % | 0.15 to 0.55 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.4 |
| Palladium (Pd), % | 0 | |
| 0.12 to 0.3 |
| Silicon (Si), % | 8.3 to 9.7 | |
| 0 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Titanium (Ti), % | 0 to 0.2 | |
| 98.8 to 99.9 |
| Zinc (Zn), % | 0 to 0.8 | |
| 0 |
| Residuals, % | 0 to 0.25 | |
| 0 to 0.4 |