EN AC-48000 Aluminum vs. 6023 Aluminum
Both EN AC-48000 aluminum and 6023 aluminum are aluminum alloys. They have 86% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN AC-48000 aluminum and the bottom bar is 6023 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 73 | |
| 69 |
| Elongation at Break, % | 1.0 | |
| 11 |
| Fatigue Strength, MPa | 85 to 86 | |
| 120 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 28 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 310 | |
| 360 |
| Tensile Strength: Yield (Proof), MPa | 210 to 270 | |
| 300 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 570 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 160 |
| Melting Completion (Liquidus), °C | 600 | |
| 640 |
| Melting Onset (Solidus), °C | 560 | |
| 580 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 890 |
| Thermal Conductivity, W/m-K | 130 | |
| 170 |
| Thermal Expansion, µm/m-K | 21 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 33 | |
| 45 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 11 |
| Density, g/cm3 | 2.7 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 8.3 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1030 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.2 to 3.0 | |
| 38 to 39 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 to 510 | |
| 670 to 690 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 53 | |
| 49 |
| Strength to Weight: Axial, points | 23 to 33 | |
| 35 to 36 |
| Strength to Weight: Bending, points | 31 to 39 | |
| 40 |
| Thermal Diffusivity, mm2/s | 54 | |
| 67 |
| Thermal Shock Resistance, points | 10 to 15 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 80.4 to 87.2 | |
| 94 to 97.7 |
| Bismuth (Bi), % | 0 | |
| 0.3 to 0.8 |
| Copper (Cu), % | 0.8 to 1.5 | |
| 0.2 to 0.5 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0.8 to 1.5 | |
| 0.4 to 0.9 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0.2 to 0.6 |
| Nickel (Ni), % | 0.7 to 1.3 | |
| 0 |
| Silicon (Si), % | 10.5 to 13.5 | |
| 0.6 to 1.4 |
| Tin (Sn), % | 0 | |
| 0.6 to 1.2 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 0.35 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |