EN AC-48100 Aluminum vs. 444.0 Aluminum

Both EN AC-48100 aluminum and 444.0 aluminum are aluminum alloys. They have 84% of their average alloy composition in common.

For each property being compared, the top bar is EN AC-48100 aluminum and the bottom bar is 444.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 100 to 140
50
Elastic (Young's, Tensile) Modulus, GPa 76
71
Elongation at Break, % 1.1
25
Fatigue Strength, MPa 120 to 130
51
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 29
27
Tensile Strength: Ultimate (UTS), MPa 240 to 330
190
Tensile Strength: Yield (Proof), MPa 190 to 300
83

Thermal Properties

Latent Heat of Fusion, J/g 640
500
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 580
610
Melting Onset (Solidus), °C 470
600
Specific Heat Capacity, J/kg-K 880
900
Thermal Conductivity, W/m-K 130
160
Thermal Expansion, µm/m-K 20
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
40
Electrical Conductivity: Equal Weight (Specific), % IACS 87
140

Otherwise Unclassified Properties

Base Metal Price, % relative 11
9.5
Density, g/cm3 2.8
2.6
Embodied Carbon, kg CO2/kg material 7.3
7.9
Embodied Energy, MJ/kg 130
150
Embodied Water, L/kg 940
1110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.3 to 3.6
39
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 580
49
Stiffness to Weight: Axial, points 15
15
Stiffness to Weight: Bending, points 51
53
Strength to Weight: Axial, points 24 to 33
20
Strength to Weight: Bending, points 31 to 38
28
Thermal Diffusivity, mm2/s 55
67
Thermal Shock Resistance, points 11 to 16
8.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 72.1 to 79.8
90.5 to 93.5
Copper (Cu), % 4.0 to 5.0
0 to 0.25
Iron (Fe), % 0 to 1.3
0 to 0.6
Magnesium (Mg), % 0.25 to 0.65
0 to 0.1
Manganese (Mn), % 0 to 0.5
0 to 0.35
Nickel (Ni), % 0 to 0.3
0
Silicon (Si), % 16 to 18
6.5 to 7.5
Tin (Sn), % 0 to 0.15
0
Titanium (Ti), % 0 to 0.25
0 to 0.25
Zinc (Zn), % 0 to 1.5
0 to 0.35
Residuals, % 0 to 0.25
0 to 0.15