EN AC-51300 Aluminum vs. 206.0 Aluminum

Both EN AC-51300 aluminum and 206.0 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN AC-51300 aluminum and the bottom bar is 206.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
95 to 110
Elastic (Young's, Tensile) Modulus, GPa 67
71
Elongation at Break, % 3.7
8.4 to 12
Fatigue Strength, MPa 78
88 to 210
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 25
27
Tensile Strength: Ultimate (UTS), MPa 190
330 to 440
Tensile Strength: Yield (Proof), MPa 110
190 to 350

Thermal Properties

Latent Heat of Fusion, J/g 400
390
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 640
650
Melting Onset (Solidus), °C 600
570
Specific Heat Capacity, J/kg-K 910
880
Thermal Conductivity, W/m-K 110
120
Thermal Expansion, µm/m-K 24
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
33
Electrical Conductivity: Equal Weight (Specific), % IACS 100
99

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
11
Density, g/cm3 2.7
3.0
Embodied Carbon, kg CO2/kg material 9.1
8.0
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1180
1150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.1
24 to 49
Resilience: Unit (Modulus of Resilience), kJ/m3 87
270 to 840
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 51
46
Strength to Weight: Axial, points 20
30 to 40
Strength to Weight: Bending, points 28
35 to 42
Thermal Diffusivity, mm2/s 45
46
Thermal Shock Resistance, points 8.6
17 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 91.4 to 95.5
93.3 to 95.3
Copper (Cu), % 0 to 0.1
4.2 to 5.0
Iron (Fe), % 0 to 0.55
0 to 0.15
Magnesium (Mg), % 4.5 to 6.5
0.15 to 0.35
Manganese (Mn), % 0 to 0.45
0.2 to 0.5
Nickel (Ni), % 0
0 to 0.050
Silicon (Si), % 0 to 0.55
0 to 0.1
Tin (Sn), % 0
0 to 0.050
Titanium (Ti), % 0 to 0.2
0.15 to 0.3
Zinc (Zn), % 0 to 0.1
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.15