EN AC-51300 Aluminum vs. 6351 Aluminum

Both EN AC-51300 aluminum and 6351 aluminum are aluminum alloys. They have a very high 95% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN AC-51300 aluminum and the bottom bar is 6351 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 67
69
Elongation at Break, % 3.7
7.8 to 18
Fatigue Strength, MPa 78
79 to 130
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 25
26
Tensile Strength: Ultimate (UTS), MPa 190
140 to 310
Tensile Strength: Yield (Proof), MPa 110
95 to 270

Thermal Properties

Latent Heat of Fusion, J/g 400
410
Maximum Temperature: Mechanical, °C 170
160
Melting Completion (Liquidus), °C 640
650
Melting Onset (Solidus), °C 600
570
Specific Heat Capacity, J/kg-K 910
900
Thermal Conductivity, W/m-K 110
180
Thermal Expansion, µm/m-K 24
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
46
Electrical Conductivity: Equal Weight (Specific), % IACS 100
150

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.7
Embodied Carbon, kg CO2/kg material 9.1
8.3
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1180
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.1
20 to 38
Resilience: Unit (Modulus of Resilience), kJ/m3 87
65 to 540
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 51
50
Strength to Weight: Axial, points 20
14 to 32
Strength to Weight: Bending, points 28
22 to 38
Thermal Diffusivity, mm2/s 45
72
Thermal Shock Resistance, points 8.6
6.1 to 14

Alloy Composition

Aluminum (Al), % 91.4 to 95.5
96 to 98.5
Copper (Cu), % 0 to 0.1
0 to 0.1
Iron (Fe), % 0 to 0.55
0 to 0.5
Magnesium (Mg), % 4.5 to 6.5
0.4 to 0.8
Manganese (Mn), % 0 to 0.45
0.4 to 0.8
Silicon (Si), % 0 to 0.55
0.7 to 1.3
Titanium (Ti), % 0 to 0.2
0 to 0.2
Zinc (Zn), % 0 to 0.1
0 to 0.2
Residuals, % 0 to 0.15
0 to 0.15