EN AC-51300 Aluminum vs. A413.0 Aluminum

Both EN AC-51300 aluminum and A413.0 aluminum are aluminum alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 87% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN AC-51300 aluminum and the bottom bar is A413.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
80
Elastic (Young's, Tensile) Modulus, GPa 67
73
Elongation at Break, % 3.7
3.5
Fatigue Strength, MPa 78
130
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 25
27
Tensile Strength: Ultimate (UTS), MPa 190
240
Tensile Strength: Yield (Proof), MPa 110
130

Thermal Properties

Latent Heat of Fusion, J/g 400
570
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 640
590
Melting Onset (Solidus), °C 600
580
Specific Heat Capacity, J/kg-K 910
900
Thermal Conductivity, W/m-K 110
120
Thermal Expansion, µm/m-K 24
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
31
Electrical Conductivity: Equal Weight (Specific), % IACS 100
110

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.6
Embodied Carbon, kg CO2/kg material 9.1
7.6
Embodied Energy, MJ/kg 150
140
Embodied Water, L/kg 1180
1040

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.1
7.1
Resilience: Unit (Modulus of Resilience), kJ/m3 87
120
Stiffness to Weight: Axial, points 14
16
Stiffness to Weight: Bending, points 51
54
Strength to Weight: Axial, points 20
25
Strength to Weight: Bending, points 28
33
Thermal Diffusivity, mm2/s 45
52
Thermal Shock Resistance, points 8.6
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 91.4 to 95.5
82.9 to 89
Copper (Cu), % 0 to 0.1
0 to 1.0
Iron (Fe), % 0 to 0.55
0 to 1.3
Magnesium (Mg), % 4.5 to 6.5
0 to 0.1
Manganese (Mn), % 0 to 0.45
0 to 0.35
Nickel (Ni), % 0
0 to 0.5
Silicon (Si), % 0 to 0.55
11 to 13
Tin (Sn), % 0
0 to 0.15
Titanium (Ti), % 0 to 0.2
0
Zinc (Zn), % 0 to 0.1
0 to 0.5
Residuals, % 0 to 0.15
0 to 0.25