EN AC-51300 Aluminum vs. EN AC-44200 Aluminum

Both EN AC-51300 aluminum and EN AC-44200 aluminum are aluminum alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 88% of their average alloy composition in common.

For each property being compared, the top bar is EN AC-51300 aluminum and the bottom bar is EN AC-44200 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
60
Elastic (Young's, Tensile) Modulus, GPa 67
72
Elongation at Break, % 3.7
6.2
Fatigue Strength, MPa 78
63
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 25
27
Tensile Strength: Ultimate (UTS), MPa 190
180
Tensile Strength: Yield (Proof), MPa 110
86

Thermal Properties

Latent Heat of Fusion, J/g 400
570
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 640
590
Melting Onset (Solidus), °C 600
580
Specific Heat Capacity, J/kg-K 910
910
Thermal Conductivity, W/m-K 110
130
Thermal Expansion, µm/m-K 24
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
35
Electrical Conductivity: Equal Weight (Specific), % IACS 100
130

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.5
Embodied Carbon, kg CO2/kg material 9.1
7.7
Embodied Energy, MJ/kg 150
140
Embodied Water, L/kg 1180
1050

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.1
9.1
Resilience: Unit (Modulus of Resilience), kJ/m3 87
51
Stiffness to Weight: Axial, points 14
16
Stiffness to Weight: Bending, points 51
55
Strength to Weight: Axial, points 20
20
Strength to Weight: Bending, points 28
28
Thermal Diffusivity, mm2/s 45
59
Thermal Shock Resistance, points 8.6
8.4

Alloy Composition

Aluminum (Al), % 91.4 to 95.5
85.2 to 89.5
Copper (Cu), % 0 to 0.1
0 to 0.050
Iron (Fe), % 0 to 0.55
0 to 0.55
Magnesium (Mg), % 4.5 to 6.5
0
Manganese (Mn), % 0 to 0.45
0 to 0.35
Silicon (Si), % 0 to 0.55
10.5 to 13.5
Titanium (Ti), % 0 to 0.2
0 to 0.15
Zinc (Zn), % 0 to 0.1
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.15