CC330G Bronze vs. EN 1.0425 Steel

CC330G bronze belongs to the copper alloys classification, while EN 1.0425 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CC330G bronze and the bottom bar is EN 1.0425 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110
140
Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 20
24
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 42
73
Tensile Strength: Ultimate (UTS), MPa 530
470
Tensile Strength: Yield (Proof), MPa 190
260

Thermal Properties

Latent Heat of Fusion, J/g 230
250
Maximum Temperature: Mechanical, °C 220
400
Melting Completion (Liquidus), °C 1050
1460
Melting Onset (Solidus), °C 1000
1420
Specific Heat Capacity, J/kg-K 430
470
Thermal Conductivity, W/m-K 62
50
Thermal Expansion, µm/m-K 18
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 14
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 15
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 29
2.2
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 3.2
1.5
Embodied Energy, MJ/kg 52
20
Embodied Water, L/kg 390
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
98
Resilience: Unit (Modulus of Resilience), kJ/m3 170
180
Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 18
17
Strength to Weight: Bending, points 17
17
Thermal Diffusivity, mm2/s 17
13
Thermal Shock Resistance, points 19
15

Alloy Composition

Aluminum (Al), % 8.0 to 10.5
0.020 to 0.024
Carbon (C), % 0
0 to 0.2
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 87 to 92
0 to 0.3
Iron (Fe), % 0 to 1.2
96.9 to 99.18
Lead (Pb), % 0 to 0.3
0
Manganese (Mn), % 0 to 0.5
0.8 to 1.4
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 0 to 1.0
0 to 0.3
Niobium (Nb), % 0
0 to 0.020
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.2
0 to 0.4
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 0 to 0.3
0
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.020
Zinc (Zn), % 0 to 0.5
0