CC332G Bronze vs. CC765S Brass
Both CC332G bronze and CC765S brass are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 65% of their average alloy composition in common.
For each property being compared, the top bar is CC332G bronze and the bottom bar is CC765S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 | |
| 130 |
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 22 | |
| 21 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 43 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 250 | |
| 220 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 140 |
| Melting Completion (Liquidus), °C | 1060 | |
| 860 |
| Melting Onset (Solidus), °C | 1010 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 400 |
| Thermal Conductivity, W/m-K | 45 | |
| 91 |
| Thermal Expansion, µm/m-K | 18 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 34 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 24 |
| Density, g/cm3 | 8.3 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 3.0 |
| Embodied Energy, MJ/kg | 55 | |
| 51 |
| Embodied Water, L/kg | 390 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 90 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 | |
| 220 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 20 | |
| 20 |
| Strength to Weight: Axial, points | 21 | |
| 19 |
| Strength to Weight: Bending, points | 19 | |
| 18 |
| Thermal Diffusivity, mm2/s | 12 | |
| 28 |
| Thermal Shock Resistance, points | 21 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 8.5 to 10.5 | |
| 0.5 to 2.5 |
| Antimony (Sb), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 80 to 86 | |
| 51 to 65 |
| Iron (Fe), % | 1.0 to 3.0 | |
| 0.5 to 2.0 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.3 to 3.0 |
| Nickel (Ni), % | 1.5 to 4.0 | |
| 0 to 6.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 to 1.0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 19.8 to 47.7 |