CC333G Bronze vs. AISI 317LMN Stainless Steel

CC333G bronze belongs to the copper alloys classification, while AISI 317LMN stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is AISI 317LMN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
190
Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 13
45
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 45
79
Tensile Strength: Ultimate (UTS), MPa 710
620
Tensile Strength: Yield (Proof), MPa 310
270

Thermal Properties

Latent Heat of Fusion, J/g 230
290
Maximum Temperature: Mechanical, °C 230
1020
Melting Completion (Liquidus), °C 1080
1460
Melting Onset (Solidus), °C 1020
1410
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 38
14
Thermal Expansion, µm/m-K 18
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 29
24
Density, g/cm3 8.3
8.0
Embodied Carbon, kg CO2/kg material 3.5
4.8
Embodied Energy, MJ/kg 56
65
Embodied Water, L/kg 380
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
230
Resilience: Unit (Modulus of Resilience), kJ/m3 410
180
Stiffness to Weight: Axial, points 8.0
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 24
22
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 10
3.8
Thermal Shock Resistance, points 24
14

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0 to 0.050
17 to 20
Copper (Cu), % 76 to 83
0
Iron (Fe), % 3.0 to 5.5
54.4 to 65.4
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0 to 2.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 3.7 to 6.0
13.5 to 17.5
Nitrogen (N), % 0
0.1 to 0.2
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.1
0 to 0.75
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0