CC333G Bronze vs. AISI 321H Stainless Steel

CC333G bronze belongs to the copper alloys classification, while AISI 321H stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is AISI 321H stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
190
Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 13
40
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 45
77
Tensile Strength: Ultimate (UTS), MPa 710
580
Tensile Strength: Yield (Proof), MPa 310
230

Thermal Properties

Latent Heat of Fusion, J/g 230
290
Maximum Temperature: Mechanical, °C 230
940
Melting Completion (Liquidus), °C 1080
1430
Melting Onset (Solidus), °C 1020
1380
Specific Heat Capacity, J/kg-K 440
480
Thermal Conductivity, W/m-K 38
15
Thermal Expansion, µm/m-K 18
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 29
16
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 3.5
3.2
Embodied Energy, MJ/kg 56
46
Embodied Water, L/kg 380
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
190
Resilience: Unit (Modulus of Resilience), kJ/m3 410
140
Stiffness to Weight: Axial, points 8.0
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 24
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 10
4.0
Thermal Shock Resistance, points 24
12

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Carbon (C), % 0
0.040 to 0.1
Chromium (Cr), % 0 to 0.050
17 to 19
Copper (Cu), % 76 to 83
0
Iron (Fe), % 3.0 to 5.5
65.4 to 74
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0 to 2.0
Nickel (Ni), % 3.7 to 6.0
9.0 to 12
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.1
0 to 0.75
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.1
0
Titanium (Ti), % 0
0 to 0.7
Zinc (Zn), % 0 to 0.5
0