CC333G Bronze vs. EN 1.3542 Stainless Steel

CC333G bronze belongs to the copper alloys classification, while EN 1.3542 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is EN 1.3542 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
220
Elastic (Young's, Tensile) Modulus, GPa 120
190
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 45
76
Tensile Strength: Ultimate (UTS), MPa 710
720

Thermal Properties

Latent Heat of Fusion, J/g 230
270
Maximum Temperature: Mechanical, °C 230
770
Melting Completion (Liquidus), °C 1080
1440
Melting Onset (Solidus), °C 1020
1390
Specific Heat Capacity, J/kg-K 440
480
Thermal Conductivity, W/m-K 38
29
Thermal Expansion, µm/m-K 18
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
3.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
3.6

Otherwise Unclassified Properties

Base Metal Price, % relative 29
7.5
Density, g/cm3 8.3
7.7
Embodied Carbon, kg CO2/kg material 3.5
2.0
Embodied Energy, MJ/kg 56
29
Embodied Water, L/kg 380
100

Common Calculations

Stiffness to Weight: Axial, points 8.0
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 24
26
Strength to Weight: Bending, points 21
23
Thermal Diffusivity, mm2/s 10
7.9
Thermal Shock Resistance, points 24
26

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Carbon (C), % 0
0.6 to 0.7
Chromium (Cr), % 0 to 0.050
12.5 to 14.5
Copper (Cu), % 76 to 83
0
Iron (Fe), % 3.0 to 5.5
82.7 to 87.5
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 3.7 to 6.0
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0