CC333G Bronze vs. EN 1.4449 Stainless Steel

CC333G bronze belongs to the copper alloys classification, while EN 1.4449 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is EN 1.4449 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
190
Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 13
48
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 45
78
Tensile Strength: Ultimate (UTS), MPa 710
620
Tensile Strength: Yield (Proof), MPa 310
250

Thermal Properties

Latent Heat of Fusion, J/g 230
290
Maximum Temperature: Mechanical, °C 230
960
Melting Completion (Liquidus), °C 1080
1440
Melting Onset (Solidus), °C 1020
1400
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 38
15
Thermal Expansion, µm/m-K 18
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 29
19
Density, g/cm3 8.3
7.9
Embodied Carbon, kg CO2/kg material 3.5
3.9
Embodied Energy, MJ/kg 56
54
Embodied Water, L/kg 380
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
240
Resilience: Unit (Modulus of Resilience), kJ/m3 410
160
Stiffness to Weight: Axial, points 8.0
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 24
22
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 10
4.0
Thermal Shock Resistance, points 24
14

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Carbon (C), % 0
0 to 0.035
Chromium (Cr), % 0 to 0.050
17 to 18.2
Copper (Cu), % 76 to 83
0 to 1.0
Iron (Fe), % 3.0 to 5.5
62.4 to 69.3
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0 to 2.0
Molybdenum (Mo), % 0
2.3 to 2.8
Nickel (Ni), % 3.7 to 6.0
11.5 to 12.5
Nitrogen (N), % 0
0 to 0.080
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0