Menu (ESC)

CC333G Bronze vs. EN 1.4919 Stainless Steel

CC333G bronze belongs to the copper alloys classification, while EN 1.4919 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is EN 1.4919 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
180
Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 13
40
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 45
78
Tensile Strength: Ultimate (UTS), MPa 710
590
Tensile Strength: Yield (Proof), MPa 310
230

Thermal Properties

Latent Heat of Fusion, J/g 230
290
Maximum Temperature: Mechanical, °C 230
950
Melting Completion (Liquidus), °C 1080
1440
Melting Onset (Solidus), °C 1020
1400
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 38
16
Thermal Expansion, µm/m-K 18
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 29
19
Density, g/cm3 8.3
7.9
Embodied Carbon, kg CO2/kg material 3.5
3.8
Embodied Energy, MJ/kg 56
52
Embodied Water, L/kg 380
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
190
Resilience: Unit (Modulus of Resilience), kJ/m3 410
130
Stiffness to Weight: Axial, points 8.0
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 24
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 10
4.3
Thermal Shock Resistance, points 24
13

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Boron (B), % 0
0.0015 to 0.0050
Carbon (C), % 0
0.040 to 0.080
Chromium (Cr), % 0 to 0.050
16.5 to 18.5
Copper (Cu), % 76 to 83
0
Iron (Fe), % 3.0 to 5.5
62.8 to 71.5
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 2.5
Nickel (Ni), % 3.7 to 6.0
10 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0