CC333G Bronze vs. EN 1.5521 Steel

CC333G bronze belongs to the copper alloys classification, while EN 1.5521 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is EN 1.5521 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
130 to 180
Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 13
11 to 21
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 45
73
Tensile Strength: Ultimate (UTS), MPa 710
430 to 1390
Tensile Strength: Yield (Proof), MPa 310
300 to 490

Thermal Properties

Latent Heat of Fusion, J/g 230
250
Maximum Temperature: Mechanical, °C 230
400
Melting Completion (Liquidus), °C 1080
1460
Melting Onset (Solidus), °C 1020
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 38
51
Thermal Expansion, µm/m-K 18
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 29
1.9
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 3.5
1.4
Embodied Energy, MJ/kg 56
19
Embodied Water, L/kg 380
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
44 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 410
250 to 630
Stiffness to Weight: Axial, points 8.0
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 24
15 to 49
Strength to Weight: Bending, points 21
16 to 35
Thermal Diffusivity, mm2/s 10
14
Thermal Shock Resistance, points 24
13 to 41

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0
0.16 to 0.2
Chromium (Cr), % 0 to 0.050
0
Copper (Cu), % 76 to 83
0 to 0.25
Iron (Fe), % 3.0 to 5.5
98 to 98.9
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0.9 to 1.2
Nickel (Ni), % 3.7 to 6.0
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.1
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0