CC333G Bronze vs. EN 1.7711 Steel

CC333G bronze belongs to the copper alloys classification, while EN 1.7711 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is EN 1.7711 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
210 to 280
Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 13
16 to 22
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 45
73
Tensile Strength: Ultimate (UTS), MPa 710
690 to 930
Tensile Strength: Yield (Proof), MPa 310
400 to 800

Thermal Properties

Latent Heat of Fusion, J/g 230
250
Maximum Temperature: Mechanical, °C 230
430
Melting Completion (Liquidus), °C 1080
1460
Melting Onset (Solidus), °C 1020
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 38
33
Thermal Expansion, µm/m-K 18
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 29
3.0
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 3.5
2.3
Embodied Energy, MJ/kg 56
32
Embodied Water, L/kg 380
54

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
130 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 410
430 to 1690
Stiffness to Weight: Axial, points 8.0
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 24
24 to 33
Strength to Weight: Bending, points 21
22 to 27
Thermal Diffusivity, mm2/s 10
8.9
Thermal Shock Resistance, points 24
24 to 32

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0 to 0.015
Bismuth (Bi), % 0 to 0.010
0
Carbon (C), % 0
0.36 to 0.44
Chromium (Cr), % 0 to 0.050
0.9 to 1.2
Copper (Cu), % 76 to 83
0
Iron (Fe), % 3.0 to 5.5
96 to 97.5
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0.45 to 0.85
Molybdenum (Mo), % 0
0.5 to 0.65
Nickel (Ni), % 3.7 to 6.0
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.1
0 to 0.4
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.1
0
Vanadium (V), % 0
0.25 to 0.35
Zinc (Zn), % 0 to 0.5
0