CC333G Bronze vs. SAE-AISI 1084 Steel

CC333G bronze belongs to the copper alloys classification, while SAE-AISI 1084 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is SAE-AISI 1084 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
220 to 270
Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 13
11
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 45
72
Tensile Strength: Ultimate (UTS), MPa 710
780 to 930
Tensile Strength: Yield (Proof), MPa 310
510 to 600

Thermal Properties

Latent Heat of Fusion, J/g 230
240
Maximum Temperature: Mechanical, °C 230
400
Melting Completion (Liquidus), °C 1080
1450
Melting Onset (Solidus), °C 1020
1410
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 38
51
Thermal Expansion, µm/m-K 18
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 29
1.8
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 3.5
1.4
Embodied Energy, MJ/kg 56
19
Embodied Water, L/kg 380
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
81 to 89
Resilience: Unit (Modulus of Resilience), kJ/m3 410
700 to 960
Stiffness to Weight: Axial, points 8.0
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 24
28 to 33
Strength to Weight: Bending, points 21
24 to 27
Thermal Diffusivity, mm2/s 10
14
Thermal Shock Resistance, points 24
25 to 30

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Carbon (C), % 0
0.8 to 0.93
Chromium (Cr), % 0 to 0.050
0
Copper (Cu), % 76 to 83
0
Iron (Fe), % 3.0 to 5.5
98.1 to 98.6
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0.6 to 0.9
Nickel (Ni), % 3.7 to 6.0
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0