MakeItFrom.com
Menu (ESC)

CC333G Bronze vs. SAE-AISI P3 Steel

CC333G bronze belongs to the copper alloys classification, while SAE-AISI P3 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is SAE-AISI P3 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 45
73
Tensile Strength: Ultimate (UTS), MPa 710
410 to 1980

Thermal Properties

Latent Heat of Fusion, J/g 230
250
Melting Completion (Liquidus), °C 1080
1460
Melting Onset (Solidus), °C 1020
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 38
46
Thermal Expansion, µm/m-K 18
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 29
2.8
Density, g/cm3 8.3
7.9
Embodied Carbon, kg CO2/kg material 3.5
1.5
Embodied Energy, MJ/kg 56
20
Embodied Water, L/kg 380
50

Common Calculations

Stiffness to Weight: Axial, points 8.0
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 24
15 to 70
Strength to Weight: Bending, points 21
16 to 44
Thermal Diffusivity, mm2/s 10
12
Thermal Shock Resistance, points 24
14 to 65

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0 to 0.050
0.4 to 0.75
Copper (Cu), % 76 to 83
0 to 0.25
Iron (Fe), % 3.0 to 5.5
96.3 to 98.4
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0.2 to 0.6
Nickel (Ni), % 3.7 to 6.0
1.0 to 1.5
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.1
0 to 0.4
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0