CC333G Bronze vs. SAE-AISI P6 Steel

CC333G bronze belongs to the copper alloys classification, while SAE-AISI P6 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is SAE-AISI P6 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 45
73
Tensile Strength: Ultimate (UTS), MPa 710
630 to 1930

Thermal Properties

Latent Heat of Fusion, J/g 230
250
Melting Completion (Liquidus), °C 1080
1460
Melting Onset (Solidus), °C 1020
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 38
43
Thermal Expansion, µm/m-K 18
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 29
4.6
Density, g/cm3 8.3
7.9
Embodied Carbon, kg CO2/kg material 3.5
1.8
Embodied Energy, MJ/kg 56
24
Embodied Water, L/kg 380
59

Common Calculations

Stiffness to Weight: Axial, points 8.0
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 24
22 to 68
Strength to Weight: Bending, points 21
21 to 44
Thermal Diffusivity, mm2/s 10
11
Thermal Shock Resistance, points 24
21 to 63

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Carbon (C), % 0
0.050 to 0.15
Chromium (Cr), % 0 to 0.050
1.3 to 1.8
Copper (Cu), % 76 to 83
0 to 0.25
Iron (Fe), % 3.0 to 5.5
92.9 to 95
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0.35 to 0.7
Nickel (Ni), % 3.7 to 6.0
3.3 to 3.8
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.1
0.1 to 0.4
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0