CC333G Bronze vs. C82800 Copper

Both CC333G bronze and C82800 copper are copper alloys. They have 80% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is C82800 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 13
1.0 to 20
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 45
46
Tensile Strength: Ultimate (UTS), MPa 710
670 to 1140
Tensile Strength: Yield (Proof), MPa 310
380 to 1000

Thermal Properties

Latent Heat of Fusion, J/g 230
240
Maximum Temperature: Mechanical, °C 230
310
Melting Completion (Liquidus), °C 1080
930
Melting Onset (Solidus), °C 1020
890
Specific Heat Capacity, J/kg-K 440
390
Thermal Conductivity, W/m-K 38
120
Thermal Expansion, µm/m-K 18
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
18
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
19

Otherwise Unclassified Properties

Density, g/cm3 8.3
8.7
Embodied Carbon, kg CO2/kg material 3.5
12
Embodied Energy, MJ/kg 56
190
Embodied Water, L/kg 380
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
11 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 410
590 to 4080
Stiffness to Weight: Axial, points 8.0
7.8
Stiffness to Weight: Bending, points 20
19
Strength to Weight: Axial, points 24
21 to 36
Strength to Weight: Bending, points 21
20 to 28
Thermal Diffusivity, mm2/s 10
36
Thermal Shock Resistance, points 24
23 to 39

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 8.5 to 10.5
0 to 0.15
Beryllium (Be), % 0
2.5 to 2.9
Bismuth (Bi), % 0 to 0.010
0
Chromium (Cr), % 0 to 0.050
0 to 0.1
Cobalt (Co), % 0
0.15 to 0.7
Copper (Cu), % 76 to 83
94.6 to 97.2
Iron (Fe), % 3.0 to 5.5
0 to 0.25
Lead (Pb), % 0 to 0.030
0 to 0.020
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0
Nickel (Ni), % 3.7 to 6.0
0 to 0.2
Silicon (Si), % 0 to 0.1
0.2 to 0.35
Tin (Sn), % 0 to 0.1
0 to 0.1
Titanium (Ti), % 0
0 to 0.12
Zinc (Zn), % 0 to 0.5
0 to 0.1
Residuals, % 0
0 to 0.5