CC333G Bronze vs. C84100 Brass

Both CC333G bronze and C84100 brass are copper alloys. They have 80% of their average alloy composition in common.

For each property being compared, the top bar is CC333G bronze and the bottom bar is C84100 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
65
Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 13
13
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 45
39
Tensile Strength: Ultimate (UTS), MPa 710
230
Tensile Strength: Yield (Proof), MPa 310
81

Thermal Properties

Latent Heat of Fusion, J/g 230
190
Maximum Temperature: Mechanical, °C 230
160
Melting Completion (Liquidus), °C 1080
1000
Melting Onset (Solidus), °C 1020
810
Specific Heat Capacity, J/kg-K 440
380
Thermal Conductivity, W/m-K 38
110
Thermal Expansion, µm/m-K 18
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
23
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
25

Otherwise Unclassified Properties

Base Metal Price, % relative 29
29
Density, g/cm3 8.3
8.5
Embodied Carbon, kg CO2/kg material 3.5
2.9
Embodied Energy, MJ/kg 56
48
Embodied Water, L/kg 380
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
24
Resilience: Unit (Modulus of Resilience), kJ/m3 410
30
Stiffness to Weight: Axial, points 8.0
7.1
Stiffness to Weight: Bending, points 20
19
Strength to Weight: Axial, points 24
7.4
Strength to Weight: Bending, points 21
9.7
Thermal Diffusivity, mm2/s 10
33
Thermal Shock Resistance, points 24
7.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 8.5 to 10.5
0 to 0.010
Antimony (Sb), % 0
0 to 0.050
Bismuth (Bi), % 0 to 0.010
0 to 0.090
Chromium (Cr), % 0 to 0.050
0
Copper (Cu), % 76 to 83
78 to 85
Iron (Fe), % 3.0 to 5.5
0 to 0.3
Lead (Pb), % 0 to 0.030
0.050 to 0.25
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0
Nickel (Ni), % 3.7 to 6.0
0 to 0.5
Phosphorus (P), % 0
0 to 0.050
Silicon (Si), % 0 to 0.1
0 to 0.010
Tin (Sn), % 0 to 0.1
1.5 to 4.5
Zinc (Zn), % 0 to 0.5
12 to 20
Residuals, % 0
0 to 0.5