CC333G Bronze vs. C91100 Bronze

Both CC333G bronze and C91100 bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 80% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is C91100 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
100
Elongation at Break, % 13
2.0
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 45
39
Tensile Strength: Ultimate (UTS), MPa 710
240
Tensile Strength: Yield (Proof), MPa 310
170

Thermal Properties

Latent Heat of Fusion, J/g 230
180
Maximum Temperature: Mechanical, °C 230
160
Melting Completion (Liquidus), °C 1080
950
Melting Onset (Solidus), °C 1020
820
Specific Heat Capacity, J/kg-K 440
360
Thermal Conductivity, W/m-K 38
63
Thermal Expansion, µm/m-K 18
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 29
38
Density, g/cm3 8.3
8.7
Embodied Carbon, kg CO2/kg material 3.5
4.2
Embodied Energy, MJ/kg 56
69
Embodied Water, L/kg 380
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
4.4
Resilience: Unit (Modulus of Resilience), kJ/m3 410
140
Stiffness to Weight: Axial, points 8.0
6.7
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 24
7.7
Strength to Weight: Bending, points 21
9.9
Thermal Diffusivity, mm2/s 10
20
Thermal Shock Resistance, points 24
9.1

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0 to 0.0050
Antimony (Sb), % 0
0 to 0.2
Bismuth (Bi), % 0 to 0.010
0
Chromium (Cr), % 0 to 0.050
0
Copper (Cu), % 76 to 83
82 to 85
Iron (Fe), % 3.0 to 5.5
0 to 0.25
Lead (Pb), % 0 to 0.030
0 to 0.25
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0
Nickel (Ni), % 3.7 to 6.0
0 to 0.5
Phosphorus (P), % 0
0 to 1.0
Silicon (Si), % 0 to 0.1
0 to 0.0050
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0 to 0.1
15 to 17
Zinc (Zn), % 0 to 0.5
0 to 0.25