CC333G Bronze vs. S31803 Stainless Steel

CC333G bronze belongs to the copper alloys classification, while S31803 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is S31803 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
260
Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 13
29
Poisson's Ratio 0.34
0.27
Shear Modulus, GPa 45
80
Tensile Strength: Ultimate (UTS), MPa 710
710
Tensile Strength: Yield (Proof), MPa 310
500

Thermal Properties

Latent Heat of Fusion, J/g 230
300
Maximum Temperature: Mechanical, °C 230
1060
Melting Completion (Liquidus), °C 1080
1450
Melting Onset (Solidus), °C 1020
1400
Specific Heat Capacity, J/kg-K 440
480
Thermal Conductivity, W/m-K 38
16
Thermal Expansion, µm/m-K 18
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 29
17
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 3.5
3.6
Embodied Energy, MJ/kg 56
49
Embodied Water, L/kg 380
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
180
Resilience: Unit (Modulus of Resilience), kJ/m3 410
630
Stiffness to Weight: Axial, points 8.0
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 24
25
Strength to Weight: Bending, points 21
23
Thermal Diffusivity, mm2/s 10
4.3
Thermal Shock Resistance, points 24
20

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0 to 0.050
21 to 23
Copper (Cu), % 76 to 83
0
Iron (Fe), % 3.0 to 5.5
63.7 to 71.9
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 3.7 to 6.0
4.5 to 6.5
Nitrogen (N), % 0
0.080 to 0.2
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0
0 to 0.020
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0