CC334G Bronze vs. Grade CW12MW Nickel
CC334G bronze belongs to the copper alloys classification, while grade CW12MW nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is CC334G bronze and the bottom bar is grade CW12MW nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 220 |
| Elongation at Break, % | 5.6 | |
| 4.6 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 45 | |
| 85 |
| Tensile Strength: Ultimate (UTS), MPa | 810 | |
| 560 |
| Tensile Strength: Yield (Proof), MPa | 410 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 240 | |
| 960 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1610 |
| Melting Onset (Solidus), °C | 1020 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 410 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 70 |
| Density, g/cm3 | 8.2 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 13 |
| Embodied Energy, MJ/kg | 59 | |
| 180 |
| Embodied Water, L/kg | 390 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 38 | |
| 22 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 710 | |
| 220 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 22 |
| Strength to Weight: Axial, points | 28 | |
| 17 |
| Strength to Weight: Bending, points | 24 | |
| 17 |
| Thermal Shock Resistance, points | 28 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 10 to 12 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.12 |
| Chromium (Cr), % | 0 | |
| 15.5 to 17.5 |
| Copper (Cu), % | 72 to 84.5 | |
| 0 |
| Iron (Fe), % | 3.0 to 7.0 | |
| 4.5 to 7.5 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 to 2.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 16 to 18 |
| Nickel (Ni), % | 4.0 to 7.5 | |
| 49.2 to 60.1 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 |
| Tungsten (W), % | 0 | |
| 3.8 to 5.3 |
| Vanadium (V), % | 0 | |
| 0.2 to 0.4 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |