CC381H Copper-nickel vs. AWS ERNiCu-7
CC381H copper-nickel belongs to the copper alloys classification, while AWS ERNiCu-7 belongs to the nickel alloys. They have 59% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is CC381H copper-nickel and the bottom bar is AWS ERNiCu-7.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 160 |
| Elongation at Break, % | 20 | |
| 34 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 52 | |
| 61 |
| Tensile Strength: Ultimate (UTS), MPa | 380 | |
| 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 280 |
| Melting Completion (Liquidus), °C | 1180 | |
| 1280 |
| Melting Onset (Solidus), °C | 1120 | |
| 1240 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 440 |
| Thermal Conductivity, W/m-K | 30 | |
| 20 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.8 | |
| 3.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.9 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 40 | |
| 50 |
| Density, g/cm3 | 8.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 5.0 | |
| 8.5 |
| Embodied Energy, MJ/kg | 73 | |
| 120 |
| Embodied Water, L/kg | 280 | |
| 250 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.6 | |
| 10 |
| Stiffness to Weight: Bending, points | 19 | |
| 21 |
| Strength to Weight: Axial, points | 12 | |
| 18 |
| Strength to Weight: Bending, points | 13 | |
| 17 |
| Thermal Diffusivity, mm2/s | 8.4 | |
| 5.3 |
| Thermal Shock Resistance, points | 13 | |
| 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.010 | |
| 0 to 1.3 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.15 |
| Copper (Cu), % | 64.5 to 69.9 | |
| 18.3 to 36.5 |
| Iron (Fe), % | 0.5 to 1.5 | |
| 0 to 2.5 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Manganese (Mn), % | 0.6 to 1.2 | |
| 0 to 4.0 |
| Nickel (Ni), % | 29 to 31 | |
| 62 to 69 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 1.3 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 1.5 to 3.0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |