CC381H Copper-nickel vs. Solder Alloy 151

CC381H copper-nickel belongs to the copper alloys classification, while solder alloy 151 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CC381H copper-nickel and the bottom bar is solder alloy 151.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
39
Elongation at Break, % 20
37
Poisson's Ratio 0.33
0.37
Shear Modulus, GPa 52
14
Tensile Strength: Ultimate (UTS), MPa 380
46

Thermal Properties

Latent Heat of Fusion, J/g 240
47
Melting Completion (Liquidus), °C 1180
150
Melting Onset (Solidus), °C 1120
150
Specific Heat Capacity, J/kg-K 410
190
Thermal Conductivity, W/m-K 30
44
Thermal Expansion, µm/m-K 16
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
10
Electrical Conductivity: Equal Weight (Specific), % IACS 6.9
10

Otherwise Unclassified Properties

Density, g/cm3 8.9
8.8
Embodied Carbon, kg CO2/kg material 5.0
9.2
Embodied Energy, MJ/kg 73
160
Embodied Water, L/kg 280
920

Common Calculations

Stiffness to Weight: Axial, points 8.6
2.5
Stiffness to Weight: Bending, points 19
13
Strength to Weight: Axial, points 12
1.4
Strength to Weight: Bending, points 13
3.2
Thermal Diffusivity, mm2/s 8.4
26
Thermal Shock Resistance, points 13
3.2

Alloy Composition

Aluminum (Al), % 0 to 0.010
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
17.5 to 18.5
Carbon (C), % 0 to 0.030
0
Copper (Cu), % 64.5 to 69.9
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0.5 to 1.5
0 to 0.020
Lead (Pb), % 0 to 0.030
30.3 to 33
Manganese (Mn), % 0.6 to 1.2
0
Nickel (Ni), % 29 to 31
0 to 0.010
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0 to 0.1
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
49.5 to 50.5
Zinc (Zn), % 0 to 0.5
0 to 0.0010