CC381H Copper-nickel vs. C97300 Nickel Silver

Both CC381H copper-nickel and C97300 nickel silver are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 69% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is CC381H copper-nickel and the bottom bar is C97300 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
110
Elongation at Break, % 20
9.0
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 52
40
Tensile Strength: Ultimate (UTS), MPa 380
230
Tensile Strength: Yield (Proof), MPa 140
110

Thermal Properties

Latent Heat of Fusion, J/g 240
180
Maximum Temperature: Mechanical, °C 260
150
Melting Completion (Liquidus), °C 1180
1040
Melting Onset (Solidus), °C 1120
1010
Specific Heat Capacity, J/kg-K 410
370
Thermal Conductivity, W/m-K 30
29
Thermal Expansion, µm/m-K 16
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
6.0
Electrical Conductivity: Equal Weight (Specific), % IACS 6.9
6.3

Otherwise Unclassified Properties

Base Metal Price, % relative 40
30
Density, g/cm3 8.9
8.6
Embodied Carbon, kg CO2/kg material 5.0
3.7
Embodied Energy, MJ/kg 73
59
Embodied Water, L/kg 280
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 60
18
Resilience: Unit (Modulus of Resilience), kJ/m3 68
59
Stiffness to Weight: Axial, points 8.6
7.0
Stiffness to Weight: Bending, points 19
18
Strength to Weight: Axial, points 12
7.6
Strength to Weight: Bending, points 13
9.8
Thermal Diffusivity, mm2/s 8.4
9.3
Thermal Shock Resistance, points 13
8.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.010
0 to 0.0050
Antimony (Sb), % 0
0 to 0.35
Carbon (C), % 0 to 0.030
0
Copper (Cu), % 64.5 to 69.9
53 to 58
Iron (Fe), % 0.5 to 1.5
0 to 1.5
Lead (Pb), % 0 to 0.030
8.0 to 11
Manganese (Mn), % 0.6 to 1.2
0
Nickel (Ni), % 29 to 31
11 to 14
Phosphorus (P), % 0 to 0.010
0 to 0.050
Silicon (Si), % 0 to 0.1
0 to 0.15
Sulfur (S), % 0 to 0.010
0 to 0.080
Tin (Sn), % 0
1.5 to 3.0
Zinc (Zn), % 0 to 0.5
17 to 25
Residuals, % 0
0 to 1.0