CC383H Copper-nickel vs. CC382H Copper-nickel

Both CC383H copper-nickel and CC382H copper-nickel are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is CC383H copper-nickel and the bottom bar is CC382H copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
130
Elastic (Young's, Tensile) Modulus, GPa 140
140
Elongation at Break, % 20
20
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 52
53
Tensile Strength: Ultimate (UTS), MPa 490
490
Tensile Strength: Yield (Proof), MPa 260
290

Thermal Properties

Latent Heat of Fusion, J/g 240
240
Maximum Temperature: Mechanical, °C 260
260
Melting Completion (Liquidus), °C 1180
1180
Melting Onset (Solidus), °C 1130
1120
Specific Heat Capacity, J/kg-K 410
410
Thermal Conductivity, W/m-K 29
30
Thermal Expansion, µm/m-K 15
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 5.2
5.5
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
5.6

Otherwise Unclassified Properties

Base Metal Price, % relative 44
41
Density, g/cm3 8.9
8.9
Embodied Carbon, kg CO2/kg material 5.7
5.2
Embodied Energy, MJ/kg 83
76
Embodied Water, L/kg 280
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84
85
Resilience: Unit (Modulus of Resilience), kJ/m3 250
290
Stiffness to Weight: Axial, points 8.6
8.8
Stiffness to Weight: Bending, points 19
20
Strength to Weight: Axial, points 15
15
Strength to Weight: Bending, points 16
16
Thermal Diffusivity, mm2/s 8.1
8.2
Thermal Shock Resistance, points 17
16

Alloy Composition

Aluminum (Al), % 0 to 0.010
0 to 0.010
Bismuth (Bi), % 0 to 0.010
0 to 0.0020
Boron (B), % 0 to 0.010
0 to 0.010
Cadmium (Cd), % 0 to 0.020
0
Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 0
1.5 to 2.0
Copper (Cu), % 64 to 69.1
62.8 to 68.4
Iron (Fe), % 0.5 to 1.5
0.5 to 1.0
Lead (Pb), % 0 to 0.010
0 to 0.0050
Magnesium (Mg), % 0 to 0.010
0 to 0.010
Manganese (Mn), % 0.6 to 1.2
0.5 to 1.0
Nickel (Ni), % 29 to 31
29 to 32
Niobium (Nb), % 0.5 to 1.0
0
Phosphorus (P), % 0 to 0.010
0 to 0.010
Selenium (Se), % 0 to 0.010
0 to 0.0050
Silicon (Si), % 0.3 to 0.7
0.15 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.010
Tellurium (Te), % 0 to 0.010
0 to 0.0050
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0 to 0.5
0 to 0.2
Zirconium (Zr), % 0
0 to 0.15