CC383H Copper-nickel vs. CC484K Bronze

Both CC383H copper-nickel and CC484K bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 69% of their average alloy composition in common.

For each property being compared, the top bar is CC383H copper-nickel and the bottom bar is CC484K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
100
Elastic (Young's, Tensile) Modulus, GPa 140
110
Elongation at Break, % 20
11
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 52
41
Tensile Strength: Ultimate (UTS), MPa 490
330
Tensile Strength: Yield (Proof), MPa 260
200

Thermal Properties

Latent Heat of Fusion, J/g 240
190
Maximum Temperature: Mechanical, °C 260
170
Melting Completion (Liquidus), °C 1180
1000
Melting Onset (Solidus), °C 1130
870
Specific Heat Capacity, J/kg-K 410
370
Thermal Conductivity, W/m-K 29
70
Thermal Expansion, µm/m-K 15
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 5.2
9.1
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
9.3

Otherwise Unclassified Properties

Base Metal Price, % relative 44
37
Density, g/cm3 8.9
8.7
Embodied Carbon, kg CO2/kg material 5.7
3.9
Embodied Energy, MJ/kg 83
64
Embodied Water, L/kg 280
400

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84
32
Resilience: Unit (Modulus of Resilience), kJ/m3 250
180
Stiffness to Weight: Axial, points 8.6
6.9
Stiffness to Weight: Bending, points 19
18
Strength to Weight: Axial, points 15
10
Strength to Weight: Bending, points 16
12
Thermal Diffusivity, mm2/s 8.1
22
Thermal Shock Resistance, points 17
12

Alloy Composition

Aluminum (Al), % 0 to 0.010
0 to 0.010
Antimony (Sb), % 0
0 to 0.1
Bismuth (Bi), % 0 to 0.010
0
Boron (B), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.020
0
Carbon (C), % 0 to 0.030
0
Copper (Cu), % 64 to 69.1
84.5 to 87.5
Iron (Fe), % 0.5 to 1.5
0 to 0.2
Lead (Pb), % 0 to 0.010
0 to 0.3
Magnesium (Mg), % 0 to 0.010
0
Manganese (Mn), % 0.6 to 1.2
0 to 0.2
Nickel (Ni), % 29 to 31
1.5 to 2.5
Niobium (Nb), % 0.5 to 1.0
0
Phosphorus (P), % 0 to 0.010
0.050 to 0.4
Selenium (Se), % 0 to 0.010
0
Silicon (Si), % 0.3 to 0.7
0 to 0.010
Sulfur (S), % 0 to 0.010
0 to 0.050
Tellurium (Te), % 0 to 0.010
0
Tin (Sn), % 0
11 to 13
Zinc (Zn), % 0 to 0.5
0 to 0.4