CC383H Copper-nickel vs. Grade 3 Babbitt Metal

CC383H copper-nickel belongs to the copper alloys classification, while grade 3 Babbitt Metal belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is CC383H copper-nickel and the bottom bar is grade 3 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
27
Elastic (Young's, Tensile) Modulus, GPa 140
56
Poisson's Ratio 0.33
0.35
Shear Modulus, GPa 52
21
Tensile Strength: Yield (Proof), MPa 260
46

Thermal Properties

Latent Heat of Fusion, J/g 240
79
Melting Completion (Liquidus), °C 1180
420
Melting Onset (Solidus), °C 1130
240
Specific Heat Capacity, J/kg-K 410
230
Thermal Expansion, µm/m-K 15
21

Otherwise Unclassified Properties

Base Metal Price, % relative 44
70
Density, g/cm3 8.9
7.4
Embodied Carbon, kg CO2/kg material 5.7
12
Embodied Energy, MJ/kg 83
200
Embodied Water, L/kg 280
1210

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 250
19
Stiffness to Weight: Axial, points 8.6
4.2
Stiffness to Weight: Bending, points 19
17

Alloy Composition

Aluminum (Al), % 0 to 0.010
0 to 0.0050
Antimony (Sb), % 0
7.5 to 8.5
Arsenic (As), % 0
0 to 0.1
Bismuth (Bi), % 0 to 0.010
0 to 0.080
Boron (B), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.020
0 to 0.050
Carbon (C), % 0 to 0.030
0
Copper (Cu), % 64 to 69.1
7.5 to 8.5
Iron (Fe), % 0.5 to 1.5
0 to 0.080
Lead (Pb), % 0 to 0.010
0 to 0.35
Magnesium (Mg), % 0 to 0.010
0
Manganese (Mn), % 0.6 to 1.2
0
Nickel (Ni), % 29 to 31
0
Niobium (Nb), % 0.5 to 1.0
0
Phosphorus (P), % 0 to 0.010
0
Selenium (Se), % 0 to 0.010
0
Silicon (Si), % 0.3 to 0.7
0
Sulfur (S), % 0 to 0.010
0
Tellurium (Te), % 0 to 0.010
0
Tin (Sn), % 0
82.3 to 85
Zinc (Zn), % 0 to 0.5
0 to 0.0050