CC383H Copper-nickel vs. C52100 Bronze

Both CC383H copper-nickel and C52100 bronze are copper alloys. They have 67% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is CC383H copper-nickel and the bottom bar is C52100 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
110
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 52
41
Tensile Strength: Ultimate (UTS), MPa 490
380 to 800

Thermal Properties

Latent Heat of Fusion, J/g 240
200
Maximum Temperature: Mechanical, °C 260
180
Melting Completion (Liquidus), °C 1180
1030
Melting Onset (Solidus), °C 1130
880
Specific Heat Capacity, J/kg-K 410
370
Thermal Conductivity, W/m-K 29
62
Thermal Expansion, µm/m-K 15
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 5.2
13
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
13

Otherwise Unclassified Properties

Base Metal Price, % relative 44
34
Density, g/cm3 8.9
8.8
Embodied Carbon, kg CO2/kg material 5.7
3.4
Embodied Energy, MJ/kg 83
55
Embodied Water, L/kg 280
370

Common Calculations

Stiffness to Weight: Axial, points 8.6
7.0
Stiffness to Weight: Bending, points 19
18
Strength to Weight: Axial, points 15
12 to 25
Strength to Weight: Bending, points 16
13 to 22
Thermal Diffusivity, mm2/s 8.1
19
Thermal Shock Resistance, points 17
14 to 28

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.010
0
Bismuth (Bi), % 0 to 0.010
0
Boron (B), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.020
0
Carbon (C), % 0 to 0.030
0
Copper (Cu), % 64 to 69.1
89.8 to 93
Iron (Fe), % 0.5 to 1.5
0 to 0.1
Lead (Pb), % 0 to 0.010
0 to 0.050
Magnesium (Mg), % 0 to 0.010
0
Manganese (Mn), % 0.6 to 1.2
0
Nickel (Ni), % 29 to 31
0
Niobium (Nb), % 0.5 to 1.0
0
Phosphorus (P), % 0 to 0.010
0.030 to 0.35
Selenium (Se), % 0 to 0.010
0
Silicon (Si), % 0.3 to 0.7
0
Sulfur (S), % 0 to 0.010
0
Tellurium (Te), % 0 to 0.010
0
Tin (Sn), % 0
7.0 to 9.0
Zinc (Zn), % 0 to 0.5
0 to 0.2
Residuals, % 0
0 to 0.5