CC383H Copper-nickel vs. C93500 Bronze

Both CC383H copper-nickel and C93500 bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 67% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is CC383H copper-nickel and the bottom bar is C93500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
100
Elongation at Break, % 20
15
Poisson's Ratio 0.33
0.35
Shear Modulus, GPa 52
38
Tensile Strength: Ultimate (UTS), MPa 490
220
Tensile Strength: Yield (Proof), MPa 260
110

Thermal Properties

Latent Heat of Fusion, J/g 240
180
Maximum Temperature: Mechanical, °C 260
160
Melting Completion (Liquidus), °C 1180
1000
Melting Onset (Solidus), °C 1130
850
Specific Heat Capacity, J/kg-K 410
360
Thermal Conductivity, W/m-K 29
70
Thermal Expansion, µm/m-K 15
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 5.2
15
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
15

Otherwise Unclassified Properties

Base Metal Price, % relative 44
31
Density, g/cm3 8.9
9.0
Embodied Carbon, kg CO2/kg material 5.7
3.0
Embodied Energy, MJ/kg 83
49
Embodied Water, L/kg 280
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84
28
Resilience: Unit (Modulus of Resilience), kJ/m3 250
59
Stiffness to Weight: Axial, points 8.6
6.3
Stiffness to Weight: Bending, points 19
17
Strength to Weight: Axial, points 15
6.9
Strength to Weight: Bending, points 16
9.1
Thermal Diffusivity, mm2/s 8.1
22
Thermal Shock Resistance, points 17
8.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.010
0 to 0.0050
Antimony (Sb), % 0
0 to 0.3
Bismuth (Bi), % 0 to 0.010
0
Boron (B), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.020
0
Carbon (C), % 0 to 0.030
0
Copper (Cu), % 64 to 69.1
83 to 86
Iron (Fe), % 0.5 to 1.5
0 to 0.2
Lead (Pb), % 0 to 0.010
8.0 to 10
Magnesium (Mg), % 0 to 0.010
0
Manganese (Mn), % 0.6 to 1.2
0
Nickel (Ni), % 29 to 31
0 to 1.0
Niobium (Nb), % 0.5 to 1.0
0
Phosphorus (P), % 0 to 0.010
0 to 1.5
Selenium (Se), % 0 to 0.010
0
Silicon (Si), % 0.3 to 0.7
0 to 0.0050
Sulfur (S), % 0 to 0.010
0 to 0.080
Tellurium (Te), % 0 to 0.010
0
Tin (Sn), % 0
4.3 to 6.0
Zinc (Zn), % 0 to 0.5
0 to 2.0
Residuals, % 0
0 to 1.0