CC481K Bronze vs. AWS ER110S-1
CC481K bronze belongs to the copper alloys classification, while AWS ER110S-1 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is CC481K bronze and the bottom bar is AWS ER110S-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 4.5 | |
| 17 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 870 |
| Tensile Strength: Yield (Proof), MPa | 180 | |
| 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 250 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1460 |
| Melting Onset (Solidus), °C | 880 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 470 |
| Thermal Conductivity, W/m-K | 64 | |
| 47 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 7.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 35 | |
| 4.0 |
| Density, g/cm3 | 8.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.7 | |
| 1.8 |
| Embodied Energy, MJ/kg | 60 | |
| 25 |
| Embodied Water, L/kg | 390 | |
| 55 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 | |
| 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 | |
| 1460 |
| Stiffness to Weight: Axial, points | 6.9 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 11 | |
| 31 |
| Strength to Weight: Bending, points | 13 | |
| 26 |
| Thermal Diffusivity, mm2/s | 20 | |
| 13 |
| Thermal Shock Resistance, points | 13 | |
| 26 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.010 | |
| 0 to 0.1 |
| Antimony (Sb), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.090 |
| Chromium (Cr), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 87 to 89.5 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.1 | |
| 92.8 to 96.3 |
| Lead (Pb), % | 0 to 0.25 | |
| 0 |
| Manganese (Mn), % | 0 to 0.050 | |
| 1.4 to 1.8 |
| Molybdenum (Mo), % | 0 | |
| 0.25 to 0.55 |
| Nickel (Ni), % | 0 to 0.1 | |
| 1.9 to 2.6 |
| Phosphorus (P), % | 0 to 1.0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.010 | |
| 0.2 to 0.55 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.010 |
| Tin (Sn), % | 10 to 11.5 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Vanadium (V), % | 0 | |
| 0 to 0.040 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.5 |